Product Features
Good gloss and scratch resistance. No tack back or cracking at room temperature. The black high-gloss grade delivers high gloss, excellent adhesion and no color separation.
Applicable Industries
Shoe material factories and related industries
Application Scope
Recoloring and spraying for TPR soles
Physical Properties
Viscosity: 4000–4500 CPS at ambient temperature
Specific Gravity: 0.910–1.200 g/ml (varies by color)
Film Thickness: 8–12 μm (adjustable upon customer request)
Adhesion: ≥4B
Pencil Hardness: ≤HB (Mitsubishi pencil)
Yellowing Resistance: Grade 4 or above
Flex Resistance: Over 60,000 cycles
Drying Time: At 50°C: surface dry 5–10 min; hard dry 12–24 h
Instructions for Use
1. Pre-treatment before spraying. The quality of pre-treatment directly affects ink adhesion. Generally, the sole surface contains contaminants such as release agents (wax-based), oil stains, hand perspiration and dust, which must be thoroughly cleaned first.
2. TPR soles are internally colored foamed products and have pinholes of varying degrees. Without putty filling treatment, it is difficult to achieve a smooth surface finish. The ink mixing ratio should neither be too thick nor too thin. Too thick will cause poor drying; too thin will reduce filling power and fail to cover tiny pinholes. Adjust the mixing ratio flexibly according to actual sole conditions.
3. Stir thoroughly before use. Seal leftover product promptly.
4. Do not mix with other paints or inks.
Precautions
1. Stir fully before use, allow to stand for 15 minutes, then filter prior to application.
2. Minimum full curing time of the ink film is 24 hours. Longer drying time may be required depending on film thickness and temperature.
3. Do not stack and package sprayed parts until solvents in the ink film have completely evaporated and the surface is non-blocking.
Product Safety
This product has been tested by multiple internationally renowned testing laboratories. Test results are well below the latest international regulatory limits.
Storage
1. Keep away from ignition sources; store in a well-ventilated and cool area.
2. Immediately reseal the container after opening if material remains unused to prevent solvent evaporation and contamination.